Nov 2020 DOI 10.14302/issn.2689-2855.jan-20-3616
Hossien Hosseini SeyedCorresponding author
Department of Chemistry, Faculty of Science, Islamshahr Branch, Islamic Azad University, Tehran, Iran, Nika Pooyesh Strategic Sciences Research Institute, NBP Economic Group, Tehran-Iran
The composites of Cu, Carbonyl iron (CI), carbon nanofiber (CNF), graphite nanoflake (GNF)/polypyrrole (PPy) and [(Cu-CI-CNF-GNF) 0.5-PAA]-PPy0.5 were synthesized via different methods by in-situ polymerization on the surface of nanoparticles (NPs) with core-shell structure. This paper describes a method for polyacrylic acid (PAA) coating of NPs in aqueous solution. Then PPy coating was performed by template polymerization on NPs-PAA. Morphology, magnetic and conductivity properties were observed via scanning electron microscopy (SEM), vibrating sample magnetometer (VSM) and four probe method, respectively. The microwave characterization of nanocomposite was evaluated through arch test based on a network analyzer. The PPy nanocomposites possessed the excellent microwave multi absorbers properties in 2-18 GHz. It was also found that nanocomposites with 50% w/w and light weight exhibit good microwave absorbing properties in 2-3 GHz and 5-14 GHz frequency, so can be used to cellphone, radio frequency and radar shielding.
Apr 2020 DOI 10.14302/issn.2689-2855.jan-20-3244
Bendjemil BadisCorresponding author
DGM, FST, University of 8 Mai 1945 of Guelma, 24000 Guelma, Algeria
Nanocomposites are worn resistant materials used in cutting tool applications. The materials are composed of ultrafine powder hard phase grains surrounded by a tough binder phase carbon nanotubes (Mo2C)1-x–(TiC)x (2≤x≤4)//1Wt% SWCNTs. Composite bicarbide Mo2C-TiC was rapidly synthesised and simultaneously consolidated by field activated sintering technique (spark plasma sintering) at which the extensive volume expansion occurred as a function of the volumic fraction from 20 to 40 vol.% of TiC powders and 1 Wt.% of SWCNTs was reinforcement of the NCMC’s. The sintered powder mixture was examined by XRD patterns, the morphology of the obtained phase was observed by SEM and the phase compositions in different regions were analyzed by EDX. The composites were processed using Field Activated Sintering Technique, spark plasma sintering (SPS) at temperatures in the range of 1700-1800°C with addicting of SWCNTs. The effects of SWCNTs addition on phases morphology, microstructure hardness and fracture toughness of the nanocomposite were investigated. The best product contained 1.0 Wt% SWCNTs from (Mo2C)1-x–(TiC)x , x= 0.2 which was sintered at 1700°C, 70 MPa for 10 min, M0.8T0.2/ 1 Wt% SWCNTs exhibit a better density, highest hardness and good ductility. Relative densification was achieved 99.5 % from the theoretical and good mechanical properties like hardness and fracture toughness (KIC=5.6 Mpa m1/2) are improved. The results were confirmed using Raman scattering resonant spectroscopy.
Mar 2020 DOI 10.14302/issn.2689-2855.jan-20-3263
Bendjemil BadisCorresponding author
DGM, FST, University of 8 Mai 1945 of Guelma, 24000 Guelma, Algeria
Nanocomposites are worn resistant materials used in cutting tool applications. The materials are composed of ultrafine powder hard phase grains surrounded by a tough binder phase carbon nanotubes (Mo2C)1-x–(TiC)x (2≤x≤4)//1Wt% SWCNTs. Composite bicarbide Mo2C-TiC was rapidly synthesised and simultaneously consolidated by field activated sintering technique (spark plasma sintering) at which the extensive volume expansion occurred as a function of the volumic fraction from 20 to 40 vol.% of TiC powders and 1 Wt.% of SWCNTs was reinforcement of the NCMC’s. The sintered powder mixture was examined by XRD patterns, the morphology of the obtained phase was observed by SEM and the phase compositions in different regions were analyzed by EDX. The composites were processed using Field Activated Sintering Technique, spark plasma sintering (SPS) at temperatures in the range of 1700-1800°C with addicting of SWCNTs. The effects of SWCNTs addition on phases morphology, microstructure hardness and fracture toughness of the nanocomposite were investigated. The best product contained 1.0 Wt% SWCNTs from (Mo2C)1-x–(TiC)x , x= 0.2 which was sintered at 1700°C, 70 MPa for 10 min, M0.8T0.2/ 1 Wt% SWCNTs exhibit a better density, highest hardness and good ductility. Relative densification was achieved 99.5 % from the theoretical and good mechanical properties like hardness and fracture toughness (KIC=5.6 Mpa m1/2) are improved. The results were confirmed using Raman scattering resonant spectroscopy.
Mar 2020 DOI 10.14302/issn.2689-2855.jan-20-3243
Bendjemil BadisCorresponding author
DGM, FST, University of 8 Mai 1945 of Guelma, 24000 Guelma, Algeria
Cubic boron nitrid (cBN) bonded TiC and alloyed with single walled carbon nanotubes (SWCNTs or NC) ceramics matrix nanocomposites (CMNCs) tools were manufacturated by a field actived sparck plasma sintering processus (FASPS). The effects of cBN-TiC ratio, carbon nanotubes and optimisation of the sintering process on the microstructure, densification in addition mechanical and vibronic properties of NC-cBN-TiC nanocomposites were studied. The results showed that for the nanocomposite cBN-TiC vol. ratio of 8:2 with 0.1 wt% NC, it was found that microhardness incresses significantly with addition of carbon nanotubes exhibited the highest microhardness and fracture toughness. After sintering of the samples at 1800 °C, 10 mn, 75 MPa of cBN–TiC1-x, x=0.8 with and without addition of 0.1 wt% NC were characterized using field emission scanning electron microscopy (FESEM) and X-ray diffraction. The samples exhibited a dense polycrystalline structure. From the resonant Raman scattering we can locate the vibration frequency of the transformation cBN to hexagonal boron nitrid (hBN) and formation of secondary hard phase TiB2to consolid the (CMNCs) tools. The final product is hBN-TiC-TiB2-NC.The best product contained cBNx-TiC1-x (x=0.8)-0.1 wt % NC which was sintered at 1800 °C, 75 MPa for 10 mn. The Vickers hardness of cBN-TiC1-x (x=0.8) incresses with NC incorporation in the matrix The indentation fracture toughness was calculated to be 12.30 MPa m1/2 for cBNx-TiC1-x (x=0.8 -0.1 wt % NC ceramics matrix nanocomposite (CMNCs) tools with excellent wear resistant will be confirmed. The wear of cBN-TiC of the composites tools have shown that this is predominantly a chemical process involving the interaction of the tool with its environment and is restricted by the formation of protective layers on the exposed faces of the tool by the addition of carbon nanotubes (NC). The wear features of tools used in fine cutting tests under identical conditions will be compared and the results will be interpreted in terms of the existing models for the wear of cBN -based nanomaterials by the effects of the additives in the modified tools